Overview SA 387 Gr 12 / SA 387 Gr 5 / SA 387 Gr 9 / SA 387 Gr 91
Certain applications with the Refining and Power Industries along with specific environments within Chemical Plants require grades which address limited corrosion and elevated temperature concerns.
SA 387 Gr 12 is utilized to address low to moderate temperature challenges. For conditions with higher elevated operating temperatures, our SA 387 Gr 5, SA 387 Gr 9 and SA 387 Gr 91 are often used. Minimum tempering temperature for these cr / mo grades are:
SA 387 Gr 12 (1150 °F)
SA 387 Gr 9 (1250 °F)
SA 387 Gr 5 (1300 °F)
SA 387 Gr 91 (1350 °F)
In the tables use SA 387 Gr 12, SA 387 Gr 5, SA 387 Gr 9, and SA 387 Gr 91
*Elements represented in percentage
Element Composition % | ||||
---|---|---|---|---|
SA 387 Grade 12 |
SA 387 Grade 5 |
SA 387 Grade 9 |
SA 387 Grade 91 |
|
Carbon, max: | ||||
Heat analysis | 0.05-0.17 | 0.15 max | 0.15 max | 0.08-0.12 |
Product analysis | 0.04-0.17 | 0.15 max | 0.15 max | 0.06-0.15 |
Manganese, max: | ||||
Heat analysis | 0.40-0.65 | 0.30-0.60 | 0.30-0.60 | 0.30-0.60 |
Product analysis | 0.35-0.73 | 0.25-0.66 | 0.25-0.66 | 0.25-0.66 |
Phosphorus, max: | ||||
Heat analysis | 0.025 | 0.025 | 0.025 | 0.020 |
Product analysis | 0.025 | 0.025 | 0.025 | 0.025 |
Sulfur, max: | ||||
Heat analysis | 0.025 | 0.025 | 0.025 | 0.010 |
Product analysis | 0.025 | 0.025 | 0.025 | 0.012 |
Silicon: | ||||
Heat analysis | 0.15-0.40 | 0.50 max | 1.00 max | 0.20-0.50 |
Product analysis | 0.13-0.45 | 0.55 max | 1.05 max | 0.18-0.56 |
Chromium: | ||||
Heat analysis | 0.80-1.15 | 4.00-6.00 | 8.00-10.00 | 8.00-9.50 |
Product analysis | 0.74-1.21 | 3.90-6.10 | 7.90-10.10 | 7.90-9.60 |
Molybdenum: | ||||
Heat analysis | 0.45-0.60 | 0.45-0.65 | 0.90-1.10 | 0.85-1.05 |
Product analysis | 0.40-0.65 | 0.40-0.70 | 0.85-1.15 | 0.80-1.10 |
SA 387 Grade 12 |
SA 387 Grade 22, 5, 9 |
|
---|---|---|
Tensile strength, ksi [MPa] | 55 to 80 [380 to 550] |
60 to 85 [415 to 585] |
Yield strength min. ksi [MPa] | 33 | 30 |
Elongation in 8 in. [200 mm], min. % | 18 | |
Elongation in 2 in. [50 mm], min. % | 22 | 18 |
Reduction of area, min % | 45 40 |
SA 387 Grade 12 |
SA 387 Grade 5, 9 |
SA 387 Grade 91 |
|
---|---|---|---|
Tensile strength, ksi [MPa] | 65 to 85 [450 to 585] |
75 to 100 [515 to 690] |
85 to 110 [585 to 760] |
Yield strength min. ksi [MPal]/(0.2% offset) | 40 [275] | 45 [310] | 60 [415] |
Elongation in 8 in. [200 mm], min. %B | 19 | … | … |
Elongation in 2 in. [50 mm], min. %B | 22 | 18 | 18 |
Reduction of area, min % | … | 45 40 |
… |